High Strength (HS) zirconia has optimal milling properties and is recom- mended for porcelain fused to zirconia framework restorations. The material accepts porcelain layering exceptionally well and its low trans- lucency perfectly covers abutments. It comes with an extremely high flexural strength (close to 1500 MPa) and higher fracture toughness for long span bridges and difficult jobs where additional strength is required
.
TYPICAL PROPERTIES OF SINTERED BODY | |
---|---|
Radioactivity | 15 Bq/ug |
Flexural Strength* | 1443 MPa |
Fracture Toughness** | 10,72 MPam1/2 |
CTE | 10.3×10¯⁶×1⁰C |
Glass transition temperature non under | 1400 ⁰C |
Chemical Solubility | 5,4 g/cm² |
Bulk Density | 6,05 g/cm3 |
ZrO2+HfO2+Y2O3 | 99.8 % |
Type II. Class 5(ISO 6872:2015)
*Highest value measured by FKG Lab Germany
**Measured Vickers Identation